FEATURES
Very lower Z-CTE
CTI≧600V
High Voltage Anti-CAF
APPLICATIONS
Electronics used in humid and dirty environment
Components on electric vehicles
OBC
GENERAL PROPERTIES
Item | IPC-TM-650 | Test Condition | Typical value | ||
Glass transition temp. | DSC | ℃ | 168 | ||
CTE,Z-axis | 2.4.24 | α1，TMA | ppm/℃ | 37 | |
α2，TMA | ppm/℃ | 210 | |||
50~260℃，TMA | % | 2.3 | |||
Decomposition Temp. | 2.4.24.6 | TGA | ℃ | 352 | |
T288 | 2.4.24.1 | TMA,copper clad | min | 30 | |
Thermal stress | 2.4.13.1 | Copper clad | sec | >120 | |
unclad | sec | >180 | |||
Water absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.2 | |
Peel Strength/18μm | 2.4.8 | as received | lb/in | 7 | |
after thermal stress | lb/in | 7 | |||
Permittivity(RC50%) | 2.5.5.9 | C-24/23/50,1G | / | 4.6 | |
Loss tagent(RC50%) | 2.5.5.9 | C-24/23/50,1G | / | 0.012 | |
Volume resistivity | 2.5.17.1 | C-96/35/90 | MΩ·cm | 1.00*107 | |
Surface resistivity | 2.5.17.1 | C-96/35/90 | MΩ | 1.75*109 | |
Arc Resistance | 2.5.1 | sec | 160 | ||
Dielectric Breakdown | 2.5.6 | D48/50+D0.5/23 | KV | 45 | |
Flexural strength | Warp | 2.4.4 | as received | MPa | 565 |
Fill | 2.4.4 | as received | MPa | 455 | |
Flame resistance | UL-94 | A&E-24/125 | / | V0 | |
CTI | C-96/20/65 | IEC-60112 | Rating | PLC0 | |
u Specification sheet:IPC-4101/130, for reference only.
u Above typical value is tasted from CCL1.0mm 7628*5,except Dk/Df,the typical value is only for reference，cannot be used as the basis for judgement.